Publisher's Synopsis
A static test method for modeling low-velocity foreign object impact events to composites would prove to be very beneficial to researchers since much more data can be obtained from a static test than from an impact test. In order to examine if this is feasible, a series of static indentation and low-velocity impact tests were carried out and compared. Square specimens of many sizes and thicknesses were utilized to cover the array of types of low velocity impact events. Laminates with a pi/4 stacking sequence were employed since this is by far the most common type of engineering laminate. Three distinct flexural rigidities -under two different boundary conditions were tested in order to obtain damage ranging from that due to large deflection to contact stresses and levels in-between to examine if the static indentation-impact comparisons are valid under the spectrum of damage modes that can be experienced. Comparisons between static indentation and low-velocity impact tests were based on the maximum applied transverse load. The dependent parameters examined included dent depth, back surface crack length, delamination area, and to a limited extent, load-deflection behavior. Results showed that no distinct differences could be seen between the static indentation tests and the low-velocity impact tests, indicating that static indentation can be used to represent a low-velocity impact event.Nettles, A. T. and Douglas, M. J.Marshall Space Flight CenterLOW SPEED; COMPOSITE MATERIALS; IMPACT TESTS; INDENTATION; STATIC TESTS; MECHANICAL PROPERTIES; CRACK PROPAGATION; DEFORMATION; DELAMINATING; BOUNDARY CONDITIONS; NONDESTRUCTIVE TESTS; TRANSVERSE LOADS...